Anticorrosive resistance to many aggressive factors, the ability to withstand the destructive effect of high temperatures in the work area, manufacturability and good workability — this is the list of the most important useful qualities of the tape KhN78T. An excellent combination of basic and auxiliary alloying materials in the composition explains its popularity and active application in many areas: from the industrial complex to the manufacture of household appliances and elements of modern design for the arrangement of residential and office premises.

composition

Virtually all the advantages of the tape ХН78Т are due to its optimally selected chemical composition.

Percentage of GOST 5632−72 .

Alloy C Ti Fe Ni Cr Mn P S Si Impurities
XH78T ≤0.12 0.15−0.36 ≤6 70−80.85 19−22 ≤0,7 ≤0,015 ≤0.012 ≤0.8 ≤0,015
Mechanical characteristics
Name of the characteristic Symbol Numeric value
Bar
Limit of proportionality (yield index for deformation of residual type), MPa ST 300
Short-term strength (limit value), MPa Sv 590−880
Relative elongation at breaking strength,% D5 40
Value of relative narrowing,% Y 50
Heat treatment Hardening in air or water (980−1100 degrees)
Physical properties
Name of the characteristic The numerical value of the parameter
The value of the elastic modulus (E), MPa 2.19
The coefficient of linear expansion, measured at a temperature of 100ºC (ах10 6), 1 / deg 12.2
Heat capacity (I), W / (mxgrade) 14.6
Density, g / cm 3 8.38
Specific electrical resistance ®, Ohmmm 2 / m 1.1

APPLICATION

The variety of products produced from the tape KhN78T and a wide range of standard sizes can satisfy any customer requirements and choose the necessary option for solving the most complex engineering problem. Most often the tape ХН78Т is used for the needs of machine-building, aviation industry, energy complex. Given the good weldability of the tape HN78T, it is actively used in the manufacture of metal structures of any shape and complexity. It is important to note that although such an alloy does not require preliminary preparation of the surface of the semi-finished product before welding, but in some particularly important cases, to ensure high strength of the joint, the structural elements are heated to two hundred or three hundred degrees. The suture zone is then heat treated to relieve the residual stresses after the welding procedure is completed.

BUY AT THE BEST PRICE

On our site we offer a wide range of products from chromium-nickel alloys. The high quality of products and the absence of intermediaries determine the most favorable conditions for the acquisition of XN78T tape for any production tasks. Delivery in the shortest time in any region of the country and abroad, the compliance of products of regulatory documentation has long won the trust of regular customers. Due to the reasonable cost and a wide range of semi-finished products, chromium-nickel alloys enjoy constant popularity in all spheres of production.