Titanium series BT, grades 6, 6C, 6C belongs to the group of α + β-alloys. Manufacture of plate, sheet, foil of BT series is standardized by GOST 19807−74, and also OST 90013−81. The alloy VT6 contains 4.5% vanadium and 6% Al, and the alloy BT6C 4% vanadium and 5% Al. Aluminum hardens the α + β phase, and vanadium stabilizes the β phase and inhibits the formation of α-2 superstructure in the α phase. Heat treatment of the alloy increases the strength to 20% without loss of ductility.

Semifinished Treatment Thickness (mm) Plasticity δ% Strength (MPa) KCU J / cm³
Sheet ВТ6с Delivery status 2−4 > 12 824 — 980 ---
Annealing 4,5−6 > 12 834−980 ---
— «- 6.5 — 10 > 10 834−980 ---
Hardening-aging 2 — 10 > 8 > 1030 ---
Sheet ВТ6с Tempering 920 ° C + 450 ° C for 2 hours 2 mm 8.5 1176 ---
Hardening-aging 450 ° C 2 h 7 mm 10.5 1150 ---
Sheet ВТ6с Д

Hot-rolled billet

Hardened billet

6 mm 10.7 936 ---
Sheet ВТ6с П
23.3 940 ---
Sheet ВТ6с 45 ° К НП
27.2 885 ---
Sheet ВТ6с Д
15.1 940 ---
Sheet ВТ6с П
10 979 ---
Sheet ВТ6с 45 ° К НП
12.6 956 ---
Plate VT6s Annealing 12 — 60 > 7 834−980 ---
Sheet ВТ6 — «- 0.3−10 mm > 8% > 882 ---
Sheet ВТ6 — «- 2−10 > 8 883 — 1080 ---
--- 1.6−3.2 D 14.1−19.6 921 — 960 ---
--- 1.6−3.2 П 13.6−19.4 926 — 959 ---
Sheet ВТ6 VSMPO Basic Technology 3.2 D 19.6 960 ---

2.5 D 14.4 944 ---

1.6 D 15.9 921 ---

3.2 П 19.4 959 ---

2.5 П 13.6 945 ---

1.6 П 15.2 926 ---
Plate VT6 Annealing 11−60 > 6 890−1080 ---
— «- 60−150 > 6 840 — 1030 ---
Plate VT6 Vacuum annealing at 750 ° C 50 mm D 10.9 935 ---

50 mm P eleven 946 ---
Plate VT6 Vacuum annealing at 750 ° C 125 mmH 6.7 856 ---

125 mm P 9.3 856 ---
Plate VT6 Vacuum annealing at 750 ° C 200 mm D 7.2 839 ---

200 mm P 8.9 837 ---
Plate ВТ6ч Annealing 730 ° 2 h
13 890 70

13 900 92

12 890 55

14 870 107

29 820 80
             

The transverse direction of the clipping of the samples is P; longitudinal — D; High-altitude — B, tangential — T.

Long-term strength is characterized by the maximum stress, which at a given temperature destroys the material, after a certain period of time.

Sheet t ° С Treatment

Long-lasting strength

(MPa) 100 hours

2−3 mm 350 ° Annealing 630
Delivery status 520

Heat resistance is characterized by the greatest stress — the creep limit, under whose influence the material is deformed by a given value at a given temperature.

Advantages

Sheet rolling brand VTCH, VT6 has sufficient heat resistance, so it can be used in a wide range of temperatures. Unique strength properties of the material are due to its balanced chemical composition and additional heat treatment. Non-magnetism, high resistance to the influence of aggressive gas-like environments (so-called gas corrosion), against the background of sufficient technological ability, determined the scope of the rolled products of the brand VTCH, VT6.

application of

Fragments of equipment for chemical engineering, structural elements working in contact with sea or chlorinated water, industrial condensate. Heat resistance, high specific strength serves as a basis for structural elements of aircraft engineering: fuselage, chassis, aileron mechanisms, fastening components, production of gas turbine engine components. Due to the corrosion resistance, heat exchange equipment, ship equipment parts, chemical reactors and containers are manufactured.

Buy at the best price

A huge selection of rolled metal products, including sheets, plates, foils of the brand VT6, VT6S, VT6CH, is designed for wholesale and retail customers on the website of the «_ _" Ltd. The convenient delivery system and constant attention to the customer will make the purchase as comfortable as possible, and the conformity of all semi-finished products of high quality standards will guarantee the reliable operation of such products in any sector of the industrial complex. A variety of parameters of titanium products presented in our warehouse will make it easy to choose the right option for a wail Any engineering ideas.